Page 11 - FT HIGH TEMPERATURE TEXTILE

SILICA HIGH SILICA HIGH
TEMPERATURE TEXTILE Service Temperature TEMPERATURE TEXTILE Service Temperature

Art No.: 7125FT218 Art No.: 7125FT200
up to 1050 C up to 1050 C
o
o
Specifications & Features: Specifications & Features:

• High-silica fabrics are new-generation • A new generation of high thermal
heat resistant material. Colors resistant material developed by Colors
• Glass fibre products with a high SiO 2 leeching the glass fibre with high
content are excellent high temperature GL silica fibre (SiO ) con tent. WH
insulators and can be used over long • High silica glass fibre material are
periods without losing the properties Sizes an excellent alternative to asbestos Sizes
and without melting and vaporising. • Have low thermal conductivity, are
• Have low thermal conductivity, are inert to majority of chemical regent.
inert to majority of chemical regent 45m/roll • Resistant to organic and acid 50m/roll
• A suitable protective textile on (except hydrofloric and phospheric),
various applications. weak alkali, water and high pressure
2x4m steam, good dye electric property 2x4m
and thermal resistance.

2x2m • Fiber Type: Silica 2x2m
• Fiber Type: Silica • Composition: 96% SiO , A1 O
• Composition:>96% SiO , A1 O 3 3.5 +/-0.5% 2 2 3
2
2
3.5+/-0.5%. Method: PP-Q-K05
• Finish: Vermiculite Coating • Finish: Vinylpolymer - White Wet
• Service Temp.: 1050°C Frayproof Treatment HIGH TEMPERATURE TEXTILES
• Melting Temp.: 1600°C • Service Temp.: 1050°C
• Color: Gold • Melting Temp.: 1600°C
• Color: White

Product Performance and Specification
Properties Metric Test Method
Weave 12H Satin
Construction (Warp) 19.0 yarn/cm DIN 53853
Thread count (Fill) 11.0 yarn/cm DIN 53853
Weight 1140 +70/-50 g/m2 DIN 12127
Thickness 1.25 mm DIN EN ISO 5084
Width 100 +2/-1 cm DIN EN 1773
Length 50m +/- 2
Tensile Strength (Warp) 4767.8 N/2.5cm EN ISO 13934.1
(Fill) 2976.1 N/2.5cm EN ISO 13934.1
Application • as insulation & protection applications, such as
sealing, packaging, protective screens
• as drop cloth for welding & fire curtains
• as reinforcement for acid resistant composites for
filtration of molten metal & furnace exhaust, etc.

www.flowtronix.com | 11